Advanced high-voltage, high-capacity cathode material designed for scientific research applications, compatible with silicon-carbon anodes for high-capacity battery cell production.
| Category | Parameter | Unit | Value |
|---|---|---|---|
| Main Content | Li | wt% | 7.9079 |
| Ni | wt% | 8.4322 | |
| Mn | wt% | 29.409 | |
| Co | wt% | 8.4643 | |
| Impurities | Fe | ppm | 0.0533 |
| Ca | ppm | 1.9011 | |
| Al | ppm | 0.9158 | |
| Zn | ppm | 1.968 | |
| Particle Size | D10 | μm | 9.058 |
| D50 | μm | 12.554 | |
| D90 | μm | 17.564 | |
| Dmax | μm | 29.764 | |
| Performance | Specific Surface Area | m²/g | 3.6226 |
| Performance | Tap Density | g/cm³ | 2.1 |
| Performance | Discharge Capacity (2.0-4.8V) | mAh/g | >300 (0.1C), 250 (1C) |
| Performance | Initial Efficiency | % | 85 |
| Performance | Voltage Drop per Cycle | mV | 0.6 (after 500 cycles) |
| Performance | Capacity Retention | % | 85 (after 500 cycles) |
|
|
| مو: | 5pcs |
| السعر: | 50-10000USD/Negotiable |
| العبوة القياسية: | bottle |
| فترة التسليم: | 5-8 working days |
| طريقة الدفع: | L/C,D/A,D/P,T/T,Western Union,MoneyGram |
| سعة العرض: | 100000pcs/month |
Advanced high-voltage, high-capacity cathode material designed for scientific research applications, compatible with silicon-carbon anodes for high-capacity battery cell production.
| Category | Parameter | Unit | Value |
|---|---|---|---|
| Main Content | Li | wt% | 7.9079 |
| Ni | wt% | 8.4322 | |
| Mn | wt% | 29.409 | |
| Co | wt% | 8.4643 | |
| Impurities | Fe | ppm | 0.0533 |
| Ca | ppm | 1.9011 | |
| Al | ppm | 0.9158 | |
| Zn | ppm | 1.968 | |
| Particle Size | D10 | μm | 9.058 |
| D50 | μm | 12.554 | |
| D90 | μm | 17.564 | |
| Dmax | μm | 29.764 | |
| Performance | Specific Surface Area | m²/g | 3.6226 |
| Performance | Tap Density | g/cm³ | 2.1 |
| Performance | Discharge Capacity (2.0-4.8V) | mAh/g | >300 (0.1C), 250 (1C) |
| Performance | Initial Efficiency | % | 85 |
| Performance | Voltage Drop per Cycle | mV | 0.6 (after 500 cycles) |
| Performance | Capacity Retention | % | 85 (after 500 cycles) |