Lithium-Ion Battery Separator (2320/2325/2400/2500) – PE Separator, Ceramic-Coated (Single/Double-Side) for Li-Sulfur, Na-K-Li Batteries
This separator is prepared by the dry process and uniaxial stretching process. The microporous structure of the film is oblong and interconnected, resulting in good conductivity. No solvents are used in the production process, making the process environmentally friendly. The longitudinal strength of the film is better than the transverse strength, and there is basically no thermal shrinkage in the transverse direction.
| Product Name | XWELL 2320 | XWELL 2325 | XWELL 2400 | XWELL 2500 |
|---|---|---|---|---|
| Description | 3-layer (PP/PE/PP) | 3-layer (PP/PE/PP) | Single-layer (PP) | Single-layer (PP) |
| Width (mm) | 60/100 | 60/100 | 60/100 | 60/100 |
| Length (m) | 100 | 100 | 100 | 100 |
| Thickness (μm) | 20 | 25 | 25 | 25 |
| Air Permeability (JIS) (Seconds) | 530 | 645 | 620 | 200 |
| Porosity (%) | 39 | 39 | 41 | 55 |
| Heat Shrinkage TD 105℃/1h (%) | 0 | 0 | 0 | 0 |
| Heat Shrinkage MD 105℃/1h (%) | 1.5 / 5 | 3.0 / 5.0 | 2.3 / 5.0 | 1.1 / 5.0 |
| Tensile Strength TD (Kg/cm²) | 156 / 115 | 150 / 80 | 140 / 70 | 130 / 80 |
| Tensile Strength MD (Kg/cm²) | 2040 / 1500 | 1900 / 1000 | 1420 / 700 | 1170 / 770 |
| Puncture Strength (gf) | 400 / 360 | 450 / 380 | 450 / 340 | 325 / 200 |
| Product Thickness (μm) | 12 |
| Product Width (mm) | 86.0 |
| Air Permeability (Sec/100ml) | 152 |
| Areal Density (g/m²) | 6.7 |
| Porosity (%) | 41 |
| Puncture Strength (g) | 502 |
| Tensile Strength MD (Kgf/cm²) | 1588 |
| Tensile Strength TD (Kgf/cm²) | 1329 |
| Elongation at Break MD (%) | 0.8 |
| Elongation at Break TD (%) | 0.2 |
Features:
Application Fields:
|
|
| Moq: | 10m |
| 価格: | 1-1000USD/Negotiable |
| 標準パッケージ: | カートンのパッケージ |
| 配達期間: | 5-7日 |
| 支払方法: | L/C、D/A、D/P、T/T、ウェスタンユニオン、マネーグラム |
| 供給容量: | 1t/月 |
Lithium-Ion Battery Separator (2320/2325/2400/2500) – PE Separator, Ceramic-Coated (Single/Double-Side) for Li-Sulfur, Na-K-Li Batteries
This separator is prepared by the dry process and uniaxial stretching process. The microporous structure of the film is oblong and interconnected, resulting in good conductivity. No solvents are used in the production process, making the process environmentally friendly. The longitudinal strength of the film is better than the transverse strength, and there is basically no thermal shrinkage in the transverse direction.
| Product Name | XWELL 2320 | XWELL 2325 | XWELL 2400 | XWELL 2500 |
|---|---|---|---|---|
| Description | 3-layer (PP/PE/PP) | 3-layer (PP/PE/PP) | Single-layer (PP) | Single-layer (PP) |
| Width (mm) | 60/100 | 60/100 | 60/100 | 60/100 |
| Length (m) | 100 | 100 | 100 | 100 |
| Thickness (μm) | 20 | 25 | 25 | 25 |
| Air Permeability (JIS) (Seconds) | 530 | 645 | 620 | 200 |
| Porosity (%) | 39 | 39 | 41 | 55 |
| Heat Shrinkage TD 105℃/1h (%) | 0 | 0 | 0 | 0 |
| Heat Shrinkage MD 105℃/1h (%) | 1.5 / 5 | 3.0 / 5.0 | 2.3 / 5.0 | 1.1 / 5.0 |
| Tensile Strength TD (Kg/cm²) | 156 / 115 | 150 / 80 | 140 / 70 | 130 / 80 |
| Tensile Strength MD (Kg/cm²) | 2040 / 1500 | 1900 / 1000 | 1420 / 700 | 1170 / 770 |
| Puncture Strength (gf) | 400 / 360 | 450 / 380 | 450 / 340 | 325 / 200 |
| Product Thickness (μm) | 12 |
| Product Width (mm) | 86.0 |
| Air Permeability (Sec/100ml) | 152 |
| Areal Density (g/m²) | 6.7 |
| Porosity (%) | 41 |
| Puncture Strength (g) | 502 |
| Tensile Strength MD (Kgf/cm²) | 1588 |
| Tensile Strength TD (Kgf/cm²) | 1329 |
| Elongation at Break MD (%) | 0.8 |
| Elongation at Break TD (%) | 0.2 |
Features:
Application Fields: